  • OD 10.5mm x L 200mm-Quartz U-tube
  • Two clear quartz U-shaped drying tubes, one with a side arm, showcasing custom glass fabrication for laboratory applications
  • Quartz U-tube highlighting excellent performance: solid weld, 1200°C heat resistance, acid/alkali corrosion resistance, high purity SiO2 ≥ 99.99%, and full custom specifications.
  • Detailed view of a quartz U-tube, showing the rounding of the tube mouth and corners, heat resistance to 1200°C, acid/alkali corrosion resistance, and high purity quartz glass.
  • Quartz U-shaped drying tubes, resistant to 1200°C, with multi-shape options and a branch pipe, emphasizing custom high-temperature/high-pressure resistance and non-polluting features.
  • A clear quartz U-shaped drying tube displayed with quality certifications including CE, ISO9001, EMC, GB, RoHS, and SGS, assuring material test and quality control.
高純度石英U字乾燥管 | 溶融石英ガス乾燥・サンプル燃焼管

高純度石英U字乾燥管 | 溶融石英ガス乾燥・サンプル燃焼管

$5.80

U字管、加熱管、およびサンプル燃焼管のカスタム製作を承ります

以下は、当社の在庫品である高温融着石英U字管です

サイズ(mm)

配送料金のお見積もりについては、お問い合わせください

ワッツアップ

U字型乾燥管

高い光透過率、優れた透過性、高い透明度、高い光線透過性

高い耐熱性、優れた熱安定性、1200℃までの耐熱

幅広いサイズ展開、全仕様対応可能、多様なサイズと仕様、包括的な品揃え

耐酸・耐アルカリ性、高い耐薬品性、優れた耐食性

製品パラメータ

製品パラメータ

製品名 高純度溶融石英U字管乾燥管
材料 高純度溶融シリカ（石英ガラス）
主な特徴 優れた光学的透明性と耐高温性を備えた耐久性のある厚肉構造を特徴としています。
アプリケーション 主に実験室において、ガス流の乾燥、精製、制御に使用されます。湿気やその他の不純物に敏感な実験環境の保護に最適です。

石英性能表

Mechanical Properties Typical Value Thermal Properties Typical Value Electrical Properties Typical Value
Density 2.2 g/cm³ Softening Point 1780°C Electrical Resistivity 7 x 107 Ω·cm
Compressive Strength 1100 MPa Annealing Point 1250°C Dielectric Strength 250 - 400 kV/cm
Flexural Strength 67 MPa Specific Heat (20-350°C) 670 J/kg·°C Dielectric Constant 3.7 - 3.9
Tensile Strength 48 MPa Thermal Conductivity (20°C) 1.4 W/m·°C Dielectric Absorption Coefficient <1 x 10-4
Poisson's Ratio 0.14 - 0.17 Refractive Index 1.4585 Dielectric Loss Tangent <1 x 10-4
Young's Modulus 72000 MPa Coefficient of Thermal Expansion 5.5 x 10-7 /°C
Shear Modulus 31000 kPa Working Temperature 1750 - 2050°C
Mohs Hardness 5.5 - 6.5 Short-Term Service Temperature 1300°C
Strain Point 1280°C Continuous Service Temperature 1100°C

完全な仕様

当社の高純度溶融石英ガラス製品は、従来のガラスと比較してわずか1/20という極めて低い熱膨張係数を誇ります。この特性により、卓越した耐熱衝撃性を実現し、急激な温度変化や繰り返しの加熱・冷却環境下でも、熱割れや破損の心配がほとんどありません

耐熱性

厚肉構造、堅牢性 & 耐久性、高純度 & 透明性、強固で信頼性の高い溶接

高い透過率

豊富な石英製品ラインナップ | お客様のニーズに合わせた特注・カスタマイズ対応